Anti-corrosion method of stainless steel screw

Stainless steel screws are made of metal, and there are four main methods for metal corrosion protection, namely the nature of the material itself, the environment in which it is used, the interface between the material and the environment, and the design of improving the metal structure. If a complete corrosion-resistant alloy is used to manufacture stainless steel screws Unless there is a special requirement, it is not realistic in terms of economic concept, or the appearance of the screw is completely isolated from the environmental elements that will cause corrosion, which may not be feasible in practice, and it may be very difficult. Improved metal structure design can improve the impact of special circumstances under certain conditions, but the design of most stainless steel screws cannot be fully modified, and its maintenance function is not permanent. Therefore, this method cannot basically deal with the problem, as long as the interface is Anti-corrosion, that is, surface anti-corrosion treatment is currently the most widely used method. The anti-corrosion treatment of stainless steel screw surface refers to the use of various methods to apply a maintenance layer on the surface of the metal. Its function is to isolate the metal from the corrosive environment to prevent the corrosion process or reduce the contact between the corrosive medium and the metal surface. The purpose of avoiding or reducing corrosion.
 The maintenance layer should be able to meet the following requests:
  1. Corrosion resistance, wear resistance, high hardness,
  2. The structure is tight and intact with small pores.
  3. It is separated from the base metal and has good adhesion.
  4. Evenly spread and have a certain thickness.
The maintenance layer is usually divided into two types: metal coating and non-metal coating. Metal coating refers to the use of a metal or alloy with strong corrosion resistance to form a maintenance layer on the surface of the easily corroded metal. This kind of coating is also called plating. There are many methods and varieties of metal coatings, the most common of which is electroplating, followed by molten metal immersion plating (hot dip plating) and chemical surface treatment. Non-metallic coating refers to the use of organic polymer materials such as paint and inorganic materials such as ceramics to form a maintenance layer on the surface of metal equipment or parts. The maintenance layer can completely isolate the base metal from the environmental medium and avoid the base metal from contact corrosion Corrosion is formed in the medium of stainless steel standard parts.

评论

发表评论

此博客中的热门博文

Is the material of stainless steel screws magnetic?

There are many types of materials for making stainless steel screws, and they can be divided into several categories according to the structure at room temperature: austenitic type: such as 304, 321, 316, 310, etc.; martensite or ferrite type: such as 430, 420, 410 Wait;   Austenite is non-magnetic or weakly magnetic, while martensite or ferrite is magnetic. Due to component segregation or improper heat treatment during smelting, a small amount of martensite or ferrite in austenitic 304 stainless steel will result. In this way, 304 stainless steel will have weak magnetic properties.     After 304 stainless steel is cold worked, the structure will also be transformed into martensite. The greater the degree of cold working deformation, the more martensite transformation and the greater the magnetic properties of the steel. Like a batch of steel belts, Φ76 tubes are produced without obvious magnetic induction, and Φ9.5 tubes are produced. Because the bending deformation...
发表评论
阅读全文

How to distinguish between high-strength nuts and ordinary nuts?

What is the difference between high-strength nuts and general nuts, in fact, you only need to understand their standards and other characteristics to easily distinguish them. The so-called high-strength nut is a special bolt with high strength and high fatigue resistance used in special equipment or engineering. Of course, generally high-strength nuts are used with high-strength bolts to achieve better application. We generally see that many bolts with M heads in the market are ordinary nuts, not high-strength nuts. The calibration side of the general hexagonal head nut is the following pattern M30, and M30 indicates the thread standard, that is, the inner diameter of the thread is 30mm. Grade 10 indicates the functional grade of the bolt, and tZn is the surface treatment method. Other types of bolts also have their own expressions, but generally threaded bolts have to use the original functional grade of "M": The functional level of the nut is divided into 3, 4, 4, 5, 5.8, 6...
1 条评论
阅读全文

How to prevent stainless steel screws from rusting

 Analysis of the causes of rusty hardware screws: 1. When the electroplating factory is electroplating hardware screws, the drying is not done, resulting in residual water vapor. Or, after drying, condensate is formed during packaging. Dongguan Electronic Screw Factory introduces to you, it causes chemical reaction, produces bad occurrence, and causes hardware screw to rust. 2. Stored in a humid place for a long time. Over time, the hardware screws will slowly be corroded and oxidized, causing serious rust. 3. When electroplating hardware screws, the electroplating is poor, and the electroplating layer is too thin. Cause rust. All in all, analyze the reasons from four aspects.   The four directions are: 1. Storage environment 2. Types of electroplating 3. How to save 4. Use environment. Therefore, we must pay attention to the key points in the use of stainless steel screws: 1. The surface of the stainless steel screw adheres to the organic juice (such as melon, vegetable, nood...